Conductor: bare
copper, tinned copper
Insulator: silicone rubber
Jacket: Fiber glass braiding with silicone resin coating
Rated temp：200℃
Rated volt：300V
Test Voltage: 2000V. 1Min
Flame test: FT 2
Mechanical properties:
Tensile strength: ≥3.45N/mm2
Elongation at break of insulation: ≥100%
Min.Bending
radius: 6×OD
Standard: UL758, UL62, UL1581
Applicable for high temperature environment such as electron, electrical
household appliance, lamps and lanterns, combustion equipment, wire harness
etc.
|
AWG
|
Conductor
|
Insulation
|
Brading thickness
|
Wire OD
|
Resist.
|
|
|
Size
|
Structure
|
OD
|
Nominal
|
OD
|
Nominal
|
Toler.
|
Ω/KM
|
|
|
NO.
|
mm2
|
No./mm
|
mm
|
mm
|
mm
|
mm
|
mm
|
mm
|
Max.
|
|
|
26
|
0.128
|
7/0.16
|
0.48
|
0.38
|
1.25
|
0.15
|
1.55
|
±0.10
|
148
|
|
|
|
|
24
|
0.205
|
7/0.20
|
0.60
|
0.38
|
1.40
|
0.15
|
1.70
|
+0.20
|
93
|
|
|
-0.10
|
|
|
22
|
0.324
|
7/0.25
|
0.75
|
0.38
|
1.55
|
0.15
|
1.85
|
+0.20
|
55
|
|
|
13/0.18
|
-0.10
|
|
|
20
|
0.519
|
7/0.31
|
0.93
|
0.38
|
1.7
|
0.15
|
2.00
|
+0.20
|
34.6
|
|
|
-0.10
|
|
|
18
|
0.823
|
7/0.39
|
1.20
|
0.38
|
2.00
|
0.15
|
2.30
|
+0.20
|
23.2
|
|
|
33/0.18
|
|
|
|
16/0.254
|
-0.10
|
|
|
16
|
1.31
|
7/0.49
|
1.50
|
0.38
|
2.30
|
0.15
|
2.60
|
+0.20
|
14.6
|
|
|
52/0.18
|
-0.10
|
|
|
20
|
0.519
|
10/0.254
|
0.96
|
0.38
|
1.75
|
0.15
|
2.05
|
+0.20
|
34.6
|
|
|
21/0.18
|
-0.10
|
|
|
18
|
0.823
|
33/0.18
|
1.20
|
0.38
|
2.00
|
0.15
|
2.30
|
+0.20
|
23.2
|
|
|
-0.10
|
|
|
16
|
1.31
|
26/0.254
|
1.55
|
0.38
|
2.35
|
0.15
|
2.65
|
+0.20
|
14.6
|
|
|
-0.10
|
|
|
26
|
0.128
|
1/0.42
|
0.42
|
0.38
|
1.20
|
0.15
|
1.50
|
±0.10
|
142
|
|
|
|
|
24
|
0.205
|
1/0.52
|
0.52
|
0.38
|
1.30
|
0.15
|
1.60
|
+0.20
|
89
|
|
|
-0.10
|
|
|
22
|
0.324
|
1/0.65
|
0.65
|
0.38
|
1.45
|
0.15
|
1.75
|
+0.20
|
54.3
|
|
|
-0.10
|
|
|
20
|
0.519
|
1/0.82
|
0.82
|
0.38
|
1.60
|
0.15
|
1.90
|
+0.20
|
33.9
|
|
|
-0.10
|
|
|
18
|
0.823
|
1/1.05
|
1.05
|
0.38
|
1.85
|
0.15
|
2.15
|
+0.20
|
21.4
|
|
|
-0.10
|
|
|
16
|
1.31
|
1/1.30
|
1.30
|
0.38
|
2.10
|
0.15
|
2.40
|
+0.20
|
13.5
|
|
|
-0.10
|
|
|